国产成人精品久久二区二区-国产成人精品久久-国产成人精品高清在线-国产成人精品电影-男女边摸边做激情视频免费-哪里可以看黄色播放免费

中文版 English National hotline: 135-1124-6523
Your current position: Home >> Performance description of steel in tempering furnace after tempering

Performance description of steel in tempering furnace after tempering


 The properties of quenched steel after tempering depend on its internal microstructure; The microstructure of steel varies depending on its chemical composition, quenching process, and tempering process. Carbon steel can achieve good mechanical properties after tempering between 100 and 250 ℃. The typical changes in mechanical properties of alloy structural steel after tempering in a tempering furnace between 200 and 700 ℃ are shown in Figure 5. From Figure 5, it can be seen that as the tempering temperature increases, the tensile strength of the steel σ B monotonically decreases; yield strength σ 0.3 first slightly increases and then decreases; Reduction of area ψ And elongation δ Continuously improving; The overall trend of toughness (using fracture toughness K1c as an indicator) is upward, but there are two minimum values between 300-400 ℃ and 500-550 ℃, which are correspondingly referred to as low-temperature tempering brittleness and high-temperature tempering brittleness. Therefore, in order to obtain good comprehensive mechanical properties, alloy structural steel is often tempered in three different temperature ranges: ultra-high strength steel is about 200-300 ℃; Spring steel at around 460 ℃; Tempering of quenched and tempered steel at 550-650 ℃. Carbon and alloy tool steels require high hardness and strength, and the tempering temperature generally does not exceed 200 ℃. Alloy structural steel, mold steel, and high-speed steel with secondary hardening during tempering are all tempered within the range of 500 to 650 ℃.

 
Tempering brittleness is a problem that must be paid attention to during tempering in tempering furnace: low temperature tempering brittleness brittleness occurs in many alloy steels after quenching to martensite at 250~400 ℃. The embrittlement that has already occurred cannot be eliminated by reheating, hence it is also known as irreversible tempering embrittlement. The causes of low-temperature tempering brittleness have been extensively studied. It is generally believed that when quenched steel is tempered at 250~400 ℃, cementite precipitates at the original austenite grain boundary or at the martensite interface, forming a thin shell, which is the main reason for low temperature tempering brittleness. Adding a certain amount of silicon to the steel can delay the formation of cementite during tempering and increase the temperature at which low-temperature tempering brittleness occurs. Therefore, ultra-high strength steel containing silicon can be tempered at 300-320 ℃ without embrittlement, which is beneficial for improving comprehensive mechanical properties.
 
High temperature tempering embrittlement refers to the phenomenon of embrittlement that occurs when many alloy steels are tempered between 500 and 550 ℃ after quenching, or when they pass through the 500 to 550 ℃ range at a slow cooling rate after tempering above 600 ℃. If reheated to a temperature above 600 ℃ and rapidly cooled, toughness can be restored, hence it is also known as reversible tempering brittleness. It has been proven that impurity elements such as P, Sn, Sb, As in steel tend to migrate towards the original austenite grain boundaries at temperatures ranging from 500 to 550 ℃, leading to high-temperature tempering brittleness; Elements such as Ni and Mn can undergo grain boundary co segregation with impurities such as P and Sb, while Cr promotes this co segregation. Therefore, these elements all exacerbate the high-temperature tempering brittleness of steel. On the contrary, the interaction between molybdenum and phosphorus hinders the segregation of phosphorus at grain boundaries, which can reduce high-temperature tempering brittleness. Rare earth elements also have a similar effect. Rapid cooling of steel after tempering in a furnace above 600 ℃ can suppress phosphorus segregation, and is often used in heat treatment operations to avoid high-temperature tempering


PrevThree Phenomena of Heating Temperature in Heat Treatment Furnace

NextProduct Usage of Well Type Gas Nitriding Furnace

Copyright © 2023 Huzhou Chuangyuan Thermal Technology Co., Ltd all reserved Web Admin >>
主站蜘蛛池模板: 最新国产午夜精品视频不卡| 国产成人亚洲精品77| 国产3344永久在线观看视频| 成人一级黄色大片| huangse视频| 成年人黄视频在线观看| 全毛片| xxxx国产视频| 俄罗斯24| 青青青视频蜜桃一区二区| 久久精品国产亚洲| 骚骚影院| 青青草视频官网| 性色小视频| 二次元摸胸| www884aa| 久久青草免费视频| 一级做a免费视频| 亚洲成人黄色在线观看| 日本高清二区| 蜜桃臀久久伊人福利| 青青草免费看| 国产精品9999| 虫爱之女动漫全免费观看| 右手影院亚洲欧美| 欧美一区亚洲二区| 亚洲精品欧美在线| 91第一页| 9久9久女女热精品视频免费观看| 青草青在线免费视频| 国产一卡2卡3卡四卡精品网站| 国产亚洲美女| 不卡午夜| 日韩美女一区| 日本高清视频在线播放| 欧美一区网站| 午夜一级在线| 99久久伊人| 我的女神本子| 欧美伊人久久大香线蕉| 久久综合狠狠综合狠狠|